365-374

• Abu-Baker, Ahmad N.
• Fischer, Peter M.

The aim of this study is to report from the analyses of a corroded iron dagger from the Iron Age city at Tall Abu al-Kharaz, Jordan Valley, and to present the conservation procedures. Preliminary condition assessment was carried out by visual examination and stereomicroscope. X-ray radiography was used to reveal surface details under the external deposits and corrosion layers. X-ray diffraction (XRD) analysis was used to identify the mineralogical composition of the corrosion products. Polarized light microscopy (PLM) was used to examine a cross-section taken from the dagger to determine its corrosion profile and internal metallographic microstructure. The dagger’s radiograph showed that the edges and tip of the dagger were its weakest and most corroded parts. XRD results showed that goethite (α-FeOOH), lepidocrocite (γ-FeOOH) and magnetite (Fe3O4) were the main corrosion products. PLM examination showed that the dagger had greatly converted into magnetite. It also showed signs of hammering, carburization and heat treatment during the manufacturing process of the artifact.The dagger was treated by immersion in an alkaline solution to extract any chloride ions present in the artifact. It was then treated with tannic acid to produce a coherent film of black ferric tannate. Finally, it was coated with Paraloid B72 to consolidate it and protect it from atmospheric humidity and corrosive ions in the environmentally uncontrolled storage area.

• History and Archaeology

• Αρχαιολογία

Iron Age, iron, dagger, archaeology, conservation, analysis, Tall, Abu al-Kharaz, XRD, microscopy, X-ray radiography, artifact

Περιέχει 11 εικόνες.

1. Argyropoulos, V., Selwyn, L.S., and Logan, J.A. (1997) Developing a conservation treatment using ethylenediamine as a corrosion inhibitor for wrought iron artifacts found at terrestrial archaeological sites. In Metal 95: Proceeding of the International Conference on Metals Conservation, I. MacLeod, L. Robbiola, and S. L. Pennec (eds.), James and James, London, 153-158.Balos, S. Arlan, B. and Pense, A (2009) Roman mystery iron blades from Serbia, Materials Characterization, vol. 60, issue 4, 271-276.Costain C. (2000) Evaluation of storage solutions for archaeological iron, Journal of the Canadian Association for Conservation, vol. 25, 11-20.Fischer, P.M. (2006) Tell Abu al-Kharaz in the Jordan Valley. Volume II: The Middle and Late Bronze Ages. Contributions to the Chronology of the Eastern Mediterranean 11, Vienna.Fischer, P.M. (2008) Tell Abu al-Kharaz in the Jordan Valley. Volume I: The Early Bronze Age. Contributions to the Chronology of the Eastern Mediterranean 16, Vienna.Fischer, P.M. (2013) Tell Abu al-Kharaz in the Jordan Valley. Volume III: The Iron Age. Contributions to the Chronology of the Eastern Mediterranean 34, Vienna.Fischer, P.M., and Bürge, T. (2013) Cultural influences of the Sea Peoples in Transjordan: The Early Iron Age at Tell Abu al-Kharaz. Zeitschrift des Deutschen Palästina Vereins, vol. 129, No 2, 132-170.Fischer, P.M. and Bürge, T. (In Press) The Swedish Jordan expedition 2013 at Tall Abu al-Kharaz. Preliminary results from area 9, 10 and 11. Opuscula. Annual of the Swedish Institutes in Athens and Rome 7.Gilberg, M. R. and Seeley, N. J. (1981) The identity of compounds containing chloride ions in marine corrosion products: a critical review, Studies in Conservation, vol. 26, No 2, 50-56.Gilberg, M. R. and Seeley, N. J. (1982) The alkaline sodium sulphite reduction process for archaeological iron: a closer look, Studies in Conservation, vol. 27, No 4, 180-184Jegdić, B., Polić-Radovanović, S., Ristić, S. and Alil, A. (2012) Corrosion stability of corrosion products on an archaeological iron artefact. International Journal of Conservation Science, vol. 3, issue 4, 241-248.Keene, S. V. (1994) Real time survival rates for treatments of archaeological iron, In Ancient and Historic Metals, D. A. Scott, J. Podanay and B. Considine (eds.), Conservation and Scientific Research, Marina Del Rey, Getty Conservation Institute, Los Angeles.Lang, J. (2005) Chapter 3 Metals. In Radiography of Cultural Material. Second edition, Lang, J. and Middleton, A. (eds.), Butterworth-Heinemann, England.Logan, J. (2007), Tannic acid treatment, Canadian Conservation institute conservation notes 9/5, https://www.cci-icc.gc.ca/resources-ressources/ccinotesicc/9-6_e.pdf, accessed on 1/7/2014.Maxwell-Hyslop, R., Stech Wheeler, T., Maddin, R. and Muhly, J. (1978) An iron dagger from tomb 240 at Tell Fara south, Levant, vol. 10, 112-115.Neff, D., Dillmann, P., Bellot-Gurlet, I. and Beranger, G. (2005) Corrosion of iron archaeological artefacts in soil: characterisation of the corrosion system, Corrosion Science, vol. 47, issue 2, 515-535.North, N. A. and Pearson, C. (1978) Washing methods for chloride removal from marine iron artefacts, Studies in Conservation, vol. 23, No 4, 174-186.Pense, A. (2000) Iron through the ages’, Materials Characterization, vol. 45, issue 4-5, 353-363.Reguer, S., Mirambet, F., Dooryhee, E., Hodeau, J., Dillmann, P. and Lagarde, P. (2009) Structural evidence for the desalination of akaganeite in the preservation of iron archaeological objects, using synchrotron X-ray powder diffraction and absorption spectroscopy, Corrosion Science, vol. 51, issue 12, 2795-2802.Rimmer, M., Watkinson, D. and Wang, Q. (2012) The efficiency of chloride extraction from archaeological iron artifacts using deoxygenated alkaline solutions, Studies in Conservation, vol. 57, No 1, 29-41.Schmutzler, B. and Eggert, G. (2010) Simplifying sodium sulphite solutions – the DBU-Project ‘Rettung vor dem Rost’. In Archaeological Iron Conservation Colloquium 2010- Extended Abstracts, G. Eggert and B. Schmutzler (Eds.), State Academy of Art and Design Stuttgart, Germany, 70-73.Scott, D. and Eggert, G. (2009) Iron and Steel in Art: Corrosion, Colorants, Conservation, Archetype Publication Ltd, London.Selwyn, L. S. (2004) Overview of archaeological iron: the corrosion problem key factors affecting treatment and gaps in current knowledge. In Metal 04: Proceedings of the International Conference on Metals Conservation, J. Ashton and D. Hallam (eds.), National Museum of Australia, Canberra, 294-306.Selwyn, L. S. and Argyropoulos, V. (2005) Removal of chloride ions from archaeological wrought iron with sodium hydroxide and ethylene diamine solutions, Studies in Conservation, vol. 50, No 2, 81-99.Selwyn, L., Sirois, P. and Argyropoulos, V. (1999) The corrosion of excavated archaeological iron with details on weeping and akaganéite, Studies in Conservation, vol. 44, No 4, 217-232.Tamura, H. (2008) The role of rusts in corrosion and corrosion protection of iron and steel, Corrosion Science, vol. 50, issue 7, 1872-1883.Turgoose, S. (1982) Post excavation changes in iron antiquities. Studies in Conservation, vol. 27, No 3, 97-101.Turgoose, S. (1985) The corrosion of archaeological iron during burial and treatment, Studies in Conservation, vol. 30, No 1, 13-18.Wang, Q., Dove, S., Shearman, F. and Smirniou, M. (2008) Evaluation of methods of chloride ion concentration determination and effectiveness of desalination treatments using sodium hydroxide and alkaline sulphite solutions, The Conservator, vol. 31, issue 1, 67-74.Watkinson, D. E. (1983) Degree of mineralization: its significance for the stability and treatment of excavated ironwork. Studies in Conservation, vol. 28, No 2, 95-90.Watkinson, D. E. (1996) Chloride extraction from archaeological iron: comparative treatment efficiencies. In Archaeological Conservation and its Consequences, A. Roy and P. Smith (eds.), International Institute for Conservation, Copenhagen, 208-212.Watkinson, D. and Al-Zahrani, A. (2008) Towards quantified assessment of aqueous chloride extraction methods for archaeological iron: de-oxygenated treatment environments, The Conservator, 31, issue 1, 75-86.